1516-1439-mr-21-06-e20180395-gf02.jpg (347.29 kB)View fileThis item contains files with download restrictions
IMAGE
1516-1439-mr-21-06-e20180395-gf03.jpg (281.09 kB)View fileThis item contains files with download restrictions
IMAGE
1516-1439-mr-21-06-e20180395-gf04.jpg (183.74 kB)View fileThis item contains files with download restrictions
IMAGE
1516-1439-mr-21-06-e20180395-gf05.jpg (226.95 kB)View fileThis item contains files with download restrictions
DATASET
Table_1.xls (5.5 kB)View fileThis item contains files with download restrictions
Next page
Previous page
1/1
Switch ViewSwitch between different file views
Thumbnail viewList viewFile view
6 filesFullscreen
Effect of Solid Solution + Double Ageing on Microstructure and Properties in the Layer by Layer of the Z-Y Interface of Inconel 718 alloys Fabricated by SLM
posted on 2018-10-17, 02:48authored byPeng Liu, Si-yu Sun, Shu-bo Xu, Mei-qing Cao, Chang Hong, Jia-ying Hu
The microstructure in the Z-Y surface of Inconel 718 alloys fabricated by selective laser melting (SLM) shows the relatively homogeneous and irregular fine grain structure after the heat treatment process of 1050ºC solid solution + double ageing. A large number of bulk precipitates were observed on the grain boundary, and the typical dendritic crystallization and Laves phases disappeared. It is possible that a large number of δ phases (NbNi3) were precipitated on the grain boundary since the enrichment effect of element Nb. The hardness in the Z-Y surface increased from 350HV to 500HV, and the residual stress was transformed from the tensile stress to compressive stress.