Graphene oxide-driven interfacial coupling in laser 3D printed PEEK/PVA scaffolds for bone regeneration
Blending Polyetheretherketone (PEEK) with Polyvinyl alcohol (PVA) is promising to obtain a composite scaffold combining the excellent biomechanical properties of PEEK and the remarkable degradability of PVA. However, the weak interfacial bonding between nonpolar PEEK and polar PVA would result in poor mechanical properties. In this study, owing to its unique amphiphilic properties, graphene oxide (GO) was employed to enhance the interfacial bonding between PEEK and PVA in PEEK/PVA scaffolds that were fabricated by laser 3D printing. On the one hand, the large π-conjugated structure of GO formed strong π-π interactions with the benzene rings in PEEK. On the other hand, the oxygen-containing groups of GO formed strong hydrogen bonds with the hydroxyl groups of PVA. As a result, the interfacial free energy between PEEK and PVA decreased from 37.4 to 29.6 mJ/m2 according to the harmonic-mean rule, and the PVA phase in PEEK matrix became much fine and uniform, indicating a reinforced interfacial bonding. Correspondingly, the strength and modulus of PEEK/PVA scaffolds increased by 97.16% and 147.06%, respectively, for a GO loading of 1%. Furthermore, the scaffolds exhibited good hydrophilicity and degradability, and promoted cell attachment and proliferation in vitro and osteogenic differentiation and bone regeneration in vivo.