Additional file 1: Figure S1. of One-Pot Method for Multifunctional Yolk Structured Nanocomposites with N-doped Carbon Shell Using Polydopamine as Precursor

Download (1.28 MB)
journal contribution
posted on 19.04.2016, 05:00 by Yanwei Zhang, Min Zhang, Lei Ding, Yongtao Wang, Jingli Xu
The TEM images of core–shell Au@SiO2@Pdop (a, b) and Au@void@C(c, d) in the ratio of ethanol and water(10:1). Figure S2. The SEM imagines of Au(a,b), Au@SiO2@Pdop(c,d), Au@void@C(e,f). Figure S3. ln (C/C0) versus time for the reduction of MB. Figure S4. The SEM imagines of Fe3O4@SiO2@Pdop(a,b), Fe3O4@void@C(c,d), CNTs@Fe3O4@SiO2@Pdop(e,f), CNTs@Fe3O4@void@C(g,h), α-Fe2O3@SiO2@Pdop(I,j), α-Fe2O3@void@C(k,l), Ag@SiO2@Pdop(m,n), Ag@void@C(o,p) at different magnetification. Figure S5 The TEM imagines of Fe3O4@SiO2@Pdop(a), Fe3O4@void@C(b), α-Fe2O3@SiO2@Pdop(c), α-Fe2O3@void@C(d), CNTs@Fe3O4@SiO2@Pdop(e), CNTs@Fe3O4@void@C(f), Ag@SiO2@Pdop(g), Ag@void@C(h) at higher magnetification. (DOCX 1310 kb)