Electron Doping and Physical Properties in the Ferromagnetic Semimetal Co3Sn2–xSbxS2
datasetposted on 19.04.2022, 20:12 authored by Yafang Li, Wang Li, Jiawei Lin, Zhongnan Guo, Fan Sun, Xin Chen, Yubo Luo, Junyou Yang, Wenxia Yuan
The ferromagnetic shandite Co3Sn2S2 has attracted great attention in physics and chemistry communities owing to its Kagome net, magnetism, and topological property. Here, for the first time, we report the effect of Sb doping on the crystal structure, magnetic interaction, and transport behavior of this ferromagnetic Weyl semimetal. A relatively low doping limit has been determined as x = 0.1 in a Co3Sn2–xSbxS2 system. Single-crystal X-ray diffraction indicates that the Sb doping shows a preferred occupation at the Sn sites between Kagome layers (Sn(1)) rather than the intralayer sites (Sn(2)), leading to the anisotropic contraction of the lattice. The ferromagnetic interaction is weakened upon Sb doping with the Curie temperature decreased from 172 to 146 K, which resulted from the shifting of the Fermi level toward high energy. Due to the electron injection, the Sb-doped sample shows the declined thermoelectric property with the reduced absolute value of the Seebeck coefficient compared to the parent compound. The anomalous Hall effect is still maintained in Co3Sn1.9Sb0.1S2 with the increased anomalous Hall resistivity based on the measurement on polycrystalline samples. Our work provides a new electron doping system to understand the interplay between the magnetism and quantum properties of this Weyl semimetal.
Read the peer-reviewed publication
seebeck coefficient comparedreduced absolute valueray diffraction indicatesdoped sample showscurie temperature decreasedchemistry communities owingattracted great attention2 )), leadingdeclined thermoelectric property1 )) rather9 </ sub3 </ subferromagnetic shandite coanomalous hall effectferromagnetic weyl semimetal2 </ subferromagnetic semimetal co1 </ subsb doping showsweyl semimetalx </ferromagnetic interaction2 –<topological propertysub ><></ subsb dopingelectron dopingwork providestransport behaviorstill maintainedquantum propertiespreferred occupationpolycrystalline samplesphysical propertiesparent compoundmagnetic interactionkagome netkagome layersintralayer sitesfirst timeelectron injectioncrystal xcrystal structureanisotropic contraction146 k