We report the synthesis of a series of indacenodithieno[3,2-b]thiophene (IDTT) based conjugated polymers by copolymerization with three different electron rich co-monomers [thiophene (T), thieno[3,2-b]thiophene (TT) and dithieno[3,2-b:2,3-d]thiophene (DTT)] under Stille coupling conditions. The resulting all donor polymeys show very good solubility in common solvents and exhibit similar optical, thermal and electronic properties. However, the performance of these semiconductors in thin film transistor devices varied and was highly dependent on the nature of the co-mnomer. All polymers exhibited unipolar p-type charge transport behaviour, with the mobility values following the trend of IDTT-TT>IDTT-DTT>IDTT-T. The peak saturation mobility value of IDTT-TT was extracted to be 1.1 cm2V-1s-1, amongst the highest mobilty for all-donor conjugated poymers reported to data
Funding
the National Natural Science Foundation of China (21464003), the Natural Science Foundation of Guangxi (2014GXNSFAA118054), the Guangxi Key Laboratory of Chemistry and Engineering of Forest Products (2013B03), the Program of Innovation Team of Guangxi Universities (GJR201147-12) and EPSRC (EP/L016702/1).the National Natural Science Foundation of China (21464003), the Natural Science Foundation of Guangxi (2014GXNSFAA118054), the Guangxi Key Laboratory of Chemistry and Engineering of Forest Products (2013B03), the Program of Innovation Team of Guangxi Universities (GJR201147-12) and EPSRC (EP/L016702/1).