ABSTRACT This study aimed to evaluate the quality of particleboards manufactured with forest exploitation waste from Pinus taeda. The material in the form of branches, tree tops, stumps and roots, was obtained from a forest plantation located in the Municipality of Mafra -SC. All the material was processed into wood chips for biomass and transported to the place of studies. The Pinus industrial particles were used as control and mixed with the waste in different proportions. The experimental plan consisted of the panels manufacture with 100% of each type of material and mixture of these com proportions of 75/25%, 50/50% and 25/75% with Pinus industrial particles, in addition to the mixture in equal parts, of the three types of materials. Experimental panels were manufactured with nominal density of 0.75 g/cm3, using the urea-formaldehyde resin, in the proportion of 8% of solids -dry weight basis of the particles. The panels were pressed with specific pressure of 4.0 MPa, temperature of 160ºC and pressing time of 8 minutes. The results of the internal bond tests met the requirements of the standard EN 312, is indicative that there has been a proper bonding of these particles originating forest exploitation wastes. General evaluations of the physical and mechanical properties results of the experimental panels indicate the possibility of use of particles obtained from branches, tree tops, stumps and roots, mixed com the industrial Pinus particles, in proportion of, up to, 50%, for particleboard manufacture.